AMS 4972 Ti 8Al - 1Mo - 1V Titanium Bar Dia45*3000mm For Aerospace stock on sale.
Titanium Alloy Bars, Wire, and Rings,8Al - 1Mo - 1V,Solution Heat Treated and Stabilized(Composition similar to UNS R54810).
AMS 4972 Ti 8Al - 1Mo - 1V,This specification covers a titanium alloy in the form of bars, wire, flash welded rings up through 4.000 inches (101.60 mm),inclusive in diameter or least distance between parallel sides, and stock for flash welded rings or heading of any size.
Application
This alloy has been used typically for parts requiring strength up to 800 °F (427 °C), but usage is not limited to such applications.
Advantage
The density of titanium is 4.506-4.516g/cm^3, melting point is 1668, boiling point is 3535. Therefore Titanium have low weight, excellent high strength and nonmagnetic festures, low density, excellent corrosion resistance features, high specificate strength and high temperature resistance features,so titanium bar is available produced, and certified to Medical (ASTM F67,ASTM F136, ISO5832-2, ISO5832-3), Aerospace (AMS 4972,AMS 4928, AMS 2631b), Industrial (ASTM B348) standards. Stock production is aligned to ASTM, AMS, and ISO standards with other standards available on made to order.
chemical Composition%
| Element | Al | Mo | V | Fe | O | C | N | H | Other Elements, each | Titanium |
| Min | 7.35 | 0.75 | 0.75 | -- | -- | -- | -- | -- | | -- |
| Max | 8.35 | 1.25 | 1.25 | 0.30 | 0.12 | 0.08 | 0.05 | 0.0150 | ≤0.1,≤0.4 | remainder |
Tensile Properties
1.At Room Temperature,determined in accordance with ASTM E8/E8M, with the rate of strain set at 0.005 in/in/min (0.005 mm/mm/min) and maintained within a tolerance of ±0.002 in/in/min (±0.002 mm/mm/min) through the 0.2% offset yield strain.
Tensile Properties At Room Temperature
| Nominal Diameter | Tensile Strength MPa | Yield Strength
at 0.2% Offset MPa | Elongation
in 4D % | Reduction of
Area % |
| 45mm | 896 | 827 | 10 | 20 |
2. At 800 °F (427 °C),determined in accordance with ASTM E21 on specimens heated to 800 °F ± 10 °F (427 °C± 6 °C), held at heat for 20 to 30 minutes before testing, and tested at 800 °F ± 10 °F (427 °C ± 6 °C).
Tensile Properties at 800 °F (427 °C)
| Nominal Diameter | Tensile Strength MPa | Yield Strength
at 0.2% Offset MPa | Elongation
in 4D % | Reduction of
Area % |
| 45mm | 621 | 483 | 10 | 25 |
Melting Practice
Alloy shall be multiple melted. The first melt shall be made by vacuum consumable electrode, nonconsumable electrode,electron beam cold hearth, or plasma arc cold hearth melting practice. The subsequent melt or melts shall be made using vacuum arc remelting (VAR) practice. Alloy additions are not permitted in the final melt cycle.
Solution Heat Treatment
Heat to a temperature within the range 1650 to 1700 °F (899 to 927 °C) or within the range 1800 to 1850 °F (982 to 1010 °C), hold at the selected temperature within ±25 °F (±14 °C) for 60 minutes ± 5 minutes, and cool at a rate equivalent to an air cool or faster.
We stock a wide range of titanium bars, including a complete commercial line and medical titanium bar. We produce our products to precise dimensions. Titanium Forged Bar, Titanium Rolled Bar, Square Titanium Bar are all available. It can be supplied in required and precise lengths.